Shock Absorber use Chrome Plating Piston Rod

Shock Absorber use Chrome Plating Piston Rod

Outer Diameter:     Ø 6mm-35mm
Total Length:     100mm -650mm
Steel Material:    SAE1035/SAE1045
Chrome Thickness:    10~25 μm
Chrome Hardness:     900 HV Min
Roughness:     Ra 0.1 Micron Max
Straightness:     0.02/400mm

  • Description
  • Inquiry

we are China shock absorber piston rod wholesale

Shock absorber piston rod specification

Outer Diameter: Ø 6mm-35mm
Total Length: 100mm -650mm
Steel Material: SAE1035/SAE1045
Chrome Thickness: 10~25 μm
Chrome Hardness: 900 HV Min
Roughness: Ra 0.1 Micron Max
Straightness: 0.02/400mm
Yield Strength According to the steel material and customer requirement
Tensile Strength According to the steel material and customer requirement
Elongation According to the steel materia
Bend Test According to customer requirement
Supply condition: 1. Hard Chrome Plated
2. QPQ Treatment
3. Induction Hardened
4. Dehydrogenation & Tempered

China shock absorber piston rod application:

Piston rod is mainly used in hydraulic pneumatic, engineering machinery, automobile manufacture with the piston rod, guide pillar plastic machinery, packaging machinery, printing machinery, roller, textile machinery, transportation machinery with axis, linear motion with the linear optical axis.

I. process introduction.

The piston rod is hard chromium plating on steel substrate surface coated with a thick layer of chromium plating and its thickness is in commonly 10 to 30 microns , using the characteristics of chromium improve parts’ performance ,such as hardness, wear resistance, heat resistance and corrosion resistant .
The process features of hard chrome plated piston rod:

  1. the cathode current efficiency is as high as 25% ~ 35%, and the deposition rate is very fast.
  2.  high hardness (900 ~ 1200HV), uniform and dense network cracks, good abrasion resistance;Microcracks can be produced, and the number of microcracks can reach 800-2000 pieces/cm (according to the need), and improve the anti-corrosion ability.
  3. good dispersion ability of the plating bath, uniform thickness of the coating, not easy to produce the phenomenon of rough blister tumor, and the appearance of chromium layer is bright and smooth;
  4. the coating has strong bonding strength with the substrate, and the pretreatment is similar to the traditional technology, and the operation is easier than the traditional process;
  5. the content of trivalent chromium in the bath is allowed to be wide, and it usually does not need to discontinue electrolysis for trivalent chromium;
  6. the plating solution contains no fluoride, no rare earth elements, and no corrosion of the workpiece without low power.

 

2. Process flow.

1). Process flow of hydraulic piston rod.
Connecting rod using 35 steel, processing technology: cold-drawn forming a turning a continuous medium frequency induction hardening, a cylindrical grinding, a fine grinding cylindrical a fine grinding cylindrical shearing section.at finishing a plating chromium to hydrogen tempering shearing section.at fine grinding.In order to improve the surface quality and corrosion resistance of piston rod, super finishing process was added before chrome plating.

China shock absorber piston rod process 1

China shock absorber piston rod process 1

2). Piston rod plating process.
Inspection before plating – pack hanging fixture – chemical degreasing, electric lift oil – water – activation pickling – water washing- the moment, the piston rod chromium plating, recycling water – water washing – unloading hanging fixture – inspection

China shock absorber piston rod process 2

China shock absorber piston rod process 2

Equipment

Test center

Packing of piston rod

Each rod will be oil treatment first , then separate by layer and layer , one by one .Each small box use VCI bag to protect from rust , then box into wooden pallet . The weight and size can be made according to customer requirement .

FAQs

Q1. Are you a Manufacture or Trading Company?
A1:We are manufacturer and we have licence to export auto parts,
we have been in this line for 10 years

Q2. What kinds of parts can you supply?
A2: 1.Shock absorber 2. Piston rod 3. Oil seal 4. Rubber parts 5. Powder metallurgy parts etc.

Q3. What is your production Lead Time?
A3:Usually it’s 30 calendar days, but it depends on PO. Quantity.

Q4. What is your payment way?
A4:We accept payment by western union, T/T, L/C. Normally,
30% deposit in advance, 70% balance before shipment

Q5. Dispatch Port ?
A5:Guangzhou, Ningbo, Shanghai
Q6. What other service can you offer?
A6:OEM service, welcome to send us the design drawing to develop a new product line.
Customized service, we can help you to design your packing.
Q7. How can I get the warranty?
A7:During the warranty period,any products damaged because of the
quality problem can be changed for free.
Q8: How can I get your sample ?
A8: First you tell us which size needed , then we try to find it from our current model , if there is current mold , the samples will be free , if there is no current mold , we can supply similar size or make new mold .

MAX Auto Parts is a China auto parts supplier and manufacturer and exporter of auto parts.

Contact Us